Abstract
The stress corrosion cracking (SCC) of pipeline steels in coating disbondment chemistry (near neutral pH solution) was studied by using slow strain rate tests (SSRT), polarization techniques, SEM and SIMS (secondary ion mass spectroscope). It was found that SCC susceptibility increased as the applied electrochemical potential and strain rates decreased. Hydrogen (H) precharging or addition of CO2 facilitated the process of SCC, suggesting that dissolution and hydrogen ingress are involved in the cracking process. SIMS analysis showed that hydrogen could diffuse into steels around the crack tip during the SCC process, which would facilitate the dissolution rate of the steel and increase SCC susceptibility. A mechanism was proposed which shows that hydrogen enhances anodic dissolution type of SCC in dilute aqueous solution. A thermodynamic analysis of the SCC process was carried out, and was found to be consistent with the experimental results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.