Abstract
In order to study the effects of dissolved hydrogen atoms and hydrogen damage on elongation of mild steel in relation to the susceptibility of iron and steel to hydrogen embrittlement, tensile tests were carried out immediately after cathodic hydrogen charging and after degassing of hydrogen at room temperature. Because cathodic hydrogen charging caused internal damage, such as microcracks (blisters) and plastic deformation owing to hydrogen precipitation, the influence of the dissolved hydrogen on the elongation was distinguished from that of hydrogen damage. The dissolved hydrogen and hydrogen damage were found to cause reversible and irreversible reductions in elongation, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: JSME international journal. Ser. A, Mechanics and material engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.