Abstract
For understanding the underlying hydrogen embrittlement mechanism in transformation-induced plasticity steels, the process of damage evolution in a model austenite/martensite dual-phase microstructure following hydrogenation was investigated through multi-scale electron channelling contrast imaging and in situ optical microscopy. Localized diffusible hydrogen in martensite causes cracking through two mechanisms: (1) interaction between {1 1 0}M localized slip and {1 1 2}M twin and (2) cracking of martensite–martensite grain interfaces. The former resulted in nanovoids along the {1 1 2}M twin. The coalescence of the nanovoids generated plate-like microvoids. The latter caused shear localization on the specific plane where the crack along the martensite/martensite boundary exists, which led to additional martensite/martensite boundary cracking.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.