Abstract
There are more than 2.5 million miles of oil and gas pipelines in the United States, totaling over 330 million girth welds below ground. During construction, girth welds are susceptible to the formation of various defects, one of which is hydrogen-assisted cracks. The synergistic impact of tensile stress, a susceptible microstructure, and atomic hydrogen can lead to hydrogen embrittlement and the formation of hydrogen cracks. This paper reviews hydrogen cracking of girth welds in carbon steel pipelines made during new construction and provides examples involving hydrogen cracking in which failure analysis techniques were used to establish the metallurgical cause of failure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.