Abstract
The hydrogen storage alloy (Mg2Ni)100� xTix (x ¼ 0, 2.5, 5.0, 7.5 and 10.0 at%) powders were synthesized from elemental powder mixture by mechanical alloying (MA) under an Ar atmosphere. The as-milled powders were examined as a function of titanium addition by X-ray diffraction and synchrotron X-ray absorption near-edge structure (XANES) techniques at various milling time. The hydrogen absorption kinetics of the 15 h as-milled powders were evaluated. The maximum hydrogen absorption content of 15 h as-milled Mg2Ni powders can be improved from 3.14 mass% to 3.88 mass% when 5.0 at% of titanium was added. The hydrogenation rate of the Mg2Ni powder was also obviously enhanced by introducing the titanium into Mg2Ni lattices. More than 20% improvement of hydrogen absorption for Mg2Ni intermetallic powders was achieved by adding titanium. [doi:10.2320/matertrans.MER2007169]
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.