Abstract
Bulk hydrogen retention and the analysis of absorption kinetics have been studied on graphite irradiated with neutrons at various conditions. Two kinds of hydrogen trapping sites may exist and be additionally produced during irradiation: interstitial cluster loop edge sites (trap 1) and carbon dangling bonds at edge surfaces of crystallites (trap 2). Neutron irradiation preferably creates trap 2 sites at lower fluences and trap 1 sites at a higher fluence. Trap 2 tends to be annealed out at high temperatures, although trap 1 is hardly decreased even at 1873 K. The activation energy of hydrogen diffusion is found to be increased from 1.04 to 1.60 eV by neutron irradiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.