Abstract
A new method was developed to fabricate ultrafine cobalt nanoparticles with an average diameter of 2.8 nm from large precursory cobalt nanoparticles (around 20 nm). The obtained ultrafine nanoparticles have a narrow size distribution and a much higher Co/B ratio than that of precursory cobalt nanoparticles (almost 100 times higher). The 2.8 nm cobalt nanoparticles were used to catalyze hydroformylation of 1-hexene and syngas (CO: H 2 = 1) at 100 °C and 2.4 MPa, resulting in an average TOF (turnover frequency) of 130 h −1. Through the mercury poisoning experiments, it was observed that the presence of Hg (0) can effectively suppress the catalytic activity of the 2.8 nm Co nanoparticle catalyst system, demonstrating that a heterogeneous catalysis mechanism was followed in the ultrafine catalyst system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.