Abstract
Belite calcium sulfoaluminate (BCSA) cements are low-CO2 building materials. However, their hydration behavior and its effect on mechanical properties have still to be clarified. Here, we report a full multitechnique study of the hydration behavior up to 120 days of nonactivated and activated BCSA laboratory-prepared clinkers, with β- or αH-belite as main phase, respectively. The effects of the amount of gypsum added were also studied. The hydration and crystallization processes are reported and discussed in detail. Finally, shrinkage/expansion data are also given. The optimum amount of gypsum was close to 10 wt %. Our study has demonstrated that β-belite reacts at a higher pace than α′H-belite, irrespective of the gypsum content. The hydration mechanism of belite determines the development of the mechanical strengths. These are much higher for activated BCSA cement, ∼65 MPa at 120 days, against ∼20 MPa for nonactivated BCSA cement, with the latter having larger amounts of stratlingite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.