Humic acid assisted stabilization of dispersed single-walled carbon nanotubes in cementitious composites

Tao Hu,Xinshuai Shi,Qian Yin,Luan Li,Hongwen Jing,Zhenlong Zhao

doi:10.1515/ntrev-2019-0046

Tao Hu, Xinshuai Shi + Show 4 more

Open Access

https://doi.org/10.1515/ntrev-2019-0046

Copy DOI

Abstract

AbstractSignificant research has been done in recent decades in the field of the dispersion of carbon nanotubes in aqueous solutions and the reinforcement of ordinary Portland cement (OPC). However, the cementitious mixture, as an alkaline environment, easily leads to the re-agglomeration of dispersed single-walled carbon nanotubes (SWCNTs) and influences their enhancing effects. Humic acid (HA) is a type of natural organic matter which can assist the stabilization of dispersed single-walled carbon nanotubes in cementitious composites. The present study characterizes the influence of HA in stabilizing the dispersion of SWCNTs by means of ultraviolet spectrophotometer tests. The fluidity of fresh cement slurry and mechanical performance of hardened OPC pastes were measured to better illustrate the dispersion of SWCNTs in real cement composites. The results not only reveal that the addition of an alkaline environment to the SWCNT suspensions results in a rapid decrease of the dispersion, but also suggest that the appropriate content of HA (0.12 wt.%) can play a significant role in stabilizing the dispersion of SWCNTs. When the mixed hybrid of SWCNTs and HA with a concentration of HA/c equal to 0.05 wt.% is used, the fluidity of the fresh cement slurry experiences a maximum decline and this mixture content of materials will dramatically increase the compressive and flexural strength by about 31% and 48%, which indicates that more SWCNTs are in a dispersed state under this concentration. SEM images further prove that a suitable HA/c can inhibit the expansion of cracks in the cementitious composites.

Highlights

Significant research has been done in recent decades in the field of the dispersion of carbon nanotubes in aqueous solutions and the reinforcement of ordinary Portland cement (OPC)
The main findings obtained are as follows: 1. It was found from UV-vis tests that the addition of an alkaline environment to the single-walled carbon nanotubes (SWCNTs) suspensions would result in a rapid decrease of the dispersion of this kind of carbon nanomaterial, and the appropriate content of Humic acid (HA) can play a significant role in stabilizing the dispersion of SWCNTs
As the HA/c rises from 0.00 wt.% to 0.20 wt.%, the fluidity of the fresh cement slurry continues to decline

Summary

Introduction

Abstract: Significant research has been done in recent decades in the field of the dispersion of carbon nanotubes in aqueous solutions and the reinforcement of ordinary Portland cement (OPC). The cementitious mixture, as an alkaline environment, leads to the re-agglomeration of dispersed single-walled carbon nanotubes (SWCNTs) and influences their enhancing effects. The results reveal that the addition of an alkaline environment to the SWCNT suspensions results in a rapid decrease of the dispersion, and suggest that the appropriate content of HA (0.12 wt.%) can play a significant role in stabilizing the dispersion of SWCNTs. When the mixed hybrid of SWCNTs and HA with a concentration of HA/c equal to 0.05 wt.% is used, the fluidity of the fresh cement slurry experiences a maximum decline and this mixture content of materials will dramatically increase the compressive and flexural strength by about 31% and 48%, which indicates that more SWCNTs are in a dispersed state under this concentration. SEM images further prove that a suitable HA/c can inhibit the expansion of cracks in the cementitious composites