Abstract
The present work deals with the influence of niobium in solid solution on the dynamic recrystallization of pure nickel. High-purity nickel and two model nickel-niobium alloys were deformed to large strains via torsion at temperatures between 800 and 1000°C. Niobium additions considerably increased the flow stress, while they lowered the strain-rate sensitivity and increased the apparent activation energy. EBSD of the steady-state microstructures revealed strong grain refinement. Substructure development was favored, whereas thermal twinning was reduced by niobium. More generally, discontinuous recrystallization kinetics were considerably decreased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.