Abstract
The plastic deformation and recrystallization behavior of the commercial magnesium alloys WE54 was analyzed using the strain rates 0.01, 0.1, 1, and 5 s−1 in the temperature range from 400 to 550 °C. The dependence of the flow stress on the temperature and the strain rate was modeled using the Garofalo hyperbolic sine equation. Thereby, the activation energy for plastic deformation of 224 kJ mol−1 was determined considering the flow stress at a strain of 0.5. The analysis revealed a stress exponent of 3.2. Furthermore, processing maps were generated by plotting the efficiency of power dissipation and the instability parameter considering different instability criteria as a function of the temperature and the strain rate. Depending on these parameters the extent of the recrystallization and the localization of the nucleation varied, significantly. At 400 °C, the recrystallization is very limited and was observed at grain boundaries (GB), shear bands (SB), and twin boundaries (TW). Increasing temperatures result in an increased recrystallized fraction, while lower strain rates promote grain boundary nucleation and reduce the amount of SBN and TW. The prediction of the processing map was verified by large scale extrusion trials, which proof that the evaluation of hot compression data can provide an effective tool to establish viable processing parameters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.