Abstract
α-Sialon powder was made from α-Si3N4, Si, Y2O3 and AIN powders by a SHS process under 3 MPa nitrogen pressure. Hot pressing of the α-Sialon powder with added 0–8 wt.% YAG (Y3Al5O12) at 2223 K for 1.5 hr under 30 MPa resulted in α/β-Sialon composites. α-Sialon content of the hot pressed sample was decreased as YAG content was increased. The number of elongated α- and β-Sialon grains was increased as the YAG content was increased. Vickers hardness of the hot pressed α/β-Sialon composites was decreased as the YAG content was increased, while both the fracture toughness and the flexural strength reached their maxima at 2 wt.% YAG addition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.