Abstract
Abstract In this study, the surface of AA-2024 alloy substrate was coated with an Al-B4C reinforced composite using hot press sintering. Al and B4C powders were synthesized by mechanical alloying. To this end, four samples were prepared. As a reference sample, AA-2024 substrate was coated with pure Al powder under 110 MPa pressure. In the other samples, the AA-2024 substrate was coated with metal matrix composites (MMCs) contained in Al-5 wt.-% B4C at 90, 110 and 130 MPa. The microstructure of the transition zone formed between the AA-2024 substrate and the coating layer of the coated samples, the microstructure of the Al/B4C MMCs coating, the macro hardness, the linear reciprocating and forth wear resistance of the coating layer were investigated. In addition, an optical microscope (OM), scanning electro microscope (SEM) images and EDS analysis of the microstructure were used. It was observed that the B4C powders were homogeneously distributed in the Al matrix in the microstructure of the coating layer. It was also found that the gaps between the grains in the microstructure of the coating layer and their size decreased with an increase in pressing pressure. Accordingly, it was concluded that macro hardness increased and weight loss decreased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.