Abstract
In this work, spark-plasma-sintered Ti-20.3Al-24.7Nb (at.-%) compact was pack rolled in different phase fields to fabricate Ti2AlNb sheets with high strength and ductility without post-heat treatment. The nano O phases in the B2 matrix contributed to the high tensile strength and ductility in a single B2 phase field. In the O + B2 phase field, the O phases remarkably increased in size and resulted in high tensile strength of 1407.1 MPa. Maintaining the O phases to nano sizes and cooperation with micro-sized α 2 phases resulted in extremely high elongation of 13.91% in the α 2+O + B2 phase field. The , , , and strengthening effects of the α 2 and O phases under different conditions were analysed in detail. Highlights Spark-plasma-sintered pre-alloyed powders are used as the raw compact before hot pack rolled Ti2AlNb sheet. Ti2AlNb sheets with good mechanical properties are obtained without any post-heat treatment. This ‘SPS pre-alloyed powder + hot pack rolling’ method has great potential in breaking the limit in sheet properties. The strengthening effects of different factors are analysed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.