Hot Extruded Polycrystalline Mg2Si with Embedded XS2 Nano-particles (X: Mo, W)

Abstract

Due to their abundant, inexpensive and non-toxic constituent elements, magnesium silicide and related alloys are attractive for large-scale thermoelectric (TE) applications in the 500–800 K temperature range, in particular for energy conversion. In this work, we propose a hot extrusion method favorable for large-scale production, where the starting materials (Mg2Si and XS2, X: W, Mo) are milled together in a sealed vial. The MoS2 nano-particles (0.5–2 at.%) act as solid lubricant during the extrusion process, thus facilitating material densification, as confirmed by density measurements based on Archimedes’ method. Scanning electron microscopy images of bulk extruded specimens show a wide distribution of grain size, covering the range from 0.1 μm to 10 μm, and energy dispersive spectroscopy shows oxygen preferentially distributed at the grain boundaries. X-ray diffraction analysis shows that the major phase is the expected cubic structure of Mg2Si. The TE properties of these extruded alloys have been measured by the Harman method between 300 K and 700 K. Resistivity values at 700 K vary between 370 μΩ m and 530 μΩ m. The ZT value reaches a maximum of 0.26 for a sample with 2 at.% MoS2. Heat conductivity is reduced for extruded samples containing MoS2, which most likely behave as scattering centers for phonons. The reason why the WS2 particles do not bring any enhancement, for either densification or heat transfer reduction, might be linked to their tendency to agglomerate. These results open the way for further investigation to optimize the processing parameters for this family of TE alloys.