Abstract
The hot compression deformation of 5356 aluminum alloy was performed with the deformation temperature 300∼500°Cand the strain rate 0.01∼10s−1 by using Gleeb1e-3500 thermal mechanical simulator. The microstructure of the alloy was analyzed by ZEISS metallographic microscope. The results show that the flow stress of 5356 aluminum alloy decreases with the increase of deformation temperature and increases with the increase of strain rate. 5356 aluminum alloy is mainly dynamic recovery under low strain rate conditions, such as 0.01 S−1, 0.1 S−1. The alloy is discontinuous dynamic recrystallization under high strain rate conditions, such as 1 S−1, 10 S−1. The hot processing map of 5356 aluminum alloy was established with the strain of 0.2∼0.5, can provide an effective data reference for the development of high-end 5356 aluminum alloy wire continuous rolling process.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.