Abstract
The deformation behavior of as-extruded Mg–9.8Gd–2.7Y–0.4Zr Mg alloy is investigated by compression test with Gleeble-3500 thermal simulator at temperature of 648–723K and strain rate of 0.01–5s−1. It is found that the flow stress behavior is described by the hyperbolic sine constitutive equation in which the determined average activation energy is 229.5kJ/mol. Through the flow stresses behavior, the processing maps describing the variation of power dissipation efficiency, is constructed as a function of temperature and strain rate. The processing maps exhibit a domain of dynamic recrystallization (DRX) occurring at the temperature of 420–450°C and strain rate of 0.01–0.1s−1, corresponding to the optimum hot working window. The instability zones of flow behavior are also recognized from the maps.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.