Abstract
Pack aluminide coatings were performed on a Ti-Al-Cr-Nb alloy doped with zirconium and yttrium having two phase of a2-Ti3Al and g-TiAl microstructure. The high activity TiAl3-based coating was developed from aluminizing process carried out at 850°C for 25 hours in a pack containing 20%-wt Al, 2%wt NH4Cl, and 78%wt Al2O3. During applications at high temperatures, the coating can degrade due to the interaction between the coated system and the environment exhibit high corrosion potentials. This study investigates the hot corrosion behavior of high-activity aluminide coated Zr-Y doped a2-Ti3Al/g-TiAlCrNb intermetallic alloy at 700°C, 800°C, and 900°C in a mixture of 90% Na2SO4 and 10% NaCl. The experimental results showed that the addition of Zr and Y in the alloy reduces significantly the hot corrosion rate of the coating as resulted from the interdiffusion of these elements from the alloy to the coatings and influence the behavior of the TiAl3-based coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.