Abstract
In this study, hot corrosion behaviours of Haynes 282 (H282), Nimonic 90 (N90), and Haynes HR160 (HR160) in LiCl-Li2O molten salt were investigated at 650 °C under argon atmosphere. The corrosion rate was in the order of H282 < N90 < HR160, depending on the morphology and structure of the scale. H282 showed a localised corrosion behaviour, while N90 showed a uniform corrosion behaviour. For HR-160, intergranular corrosion was observed. The high Cr content caused intergranular corrosion in the corrosion layer. Thus, excess Cr has a deleterious effect on the corrosion kinetics during hot corrosion in LiCl-Li2O molten salt.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.