Horizontally aligned single-walled carbon nanotube field emitters fabricated on vertically aligned multi-walled carbon nanotube electrode arrays

Abstract

Vertically aligned multi-walled carbon nanotube (MWCNT) arrays were fabricated on an anodic aluminum oxide membrane bonded to a Si wafer. After obtaining a protruding tip for the MWCNTs by etching away some oxide, they were used as electrodes in the fabrication of carbon nanotube field emitters. Long single-walled carbon nanotubes (SWCNTs) were spin coated on the MWCNT arrays of uniform height. Clean SWCNTs were suspended by attaching them to the tips of the vertically aligned MWCNT arrays. The spin coated SWCNTs function as emitters, while the MWCNT arrays function as electrodes. The field emission was greatly improved by coating gold on the MWCNT arrays and annealing at 400 °C. Our field emitter exhibits good field emission properties such as a low turn-on field (1.4 V/μm), high current density (122 mA/cm 2), and good stability (55 h for 10% degradation of current density from 400 μA/cm 2).