Abstract
An important aspect that limits the use of carbon nanotubes (CNTs) is the difficulty in obtaining homogeneously dispersed CNTs of uniform length. Hence, homogenization of multi-walled carbon nanotubes (MWCNTs) and single-walled carbon nanotubes (SWCNTs) was carried out using bullet blender and the dispersion behavior was compared with that of ultrasonication. 1% sodium dodecyl sulphate (SDS), Triton-x-100 and polyethylene glycol 4000 were used as dispersing agents during homogenization. The dispersed CNTs were studied using transmission electron microscopy, ImageJ and Raman spectroscopy. Though dispersion and reduction in length of MWCNTs were observed both with ultrasonication and homogenization, lowest length range with about 75% reduction in polydispersity index was obtained on homogenization. Longer time of ultrasonication resulted in damage to small MWCNTs. Well dispersed and shorter MWCNTs were obtained with Triton-x-100 while reduction in length was minimum with SDS. SWCNTs of less than 1 μm length could be obtained by homogenization with Triton-x-100.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.