Abstract
We have prepared metal organic deposition (MOD)-YBCO thick films by repeating the coating-pyrolysis-crystallization procedure onto ∼100-nm-thick evaporated and MOD templates. Surface morphology of the template was found to strongly affect the homoepitaxial growth of MOD-YBCO layers on the template; namely, the epitaxial growth of MOD-YBCO on the evaporated template was much easier than that on the MOD template. A 220-nm-thick epitaxial MOD-YBCO film was successfully prepared on the 100-nm-thick evaporated-YBCO template to obtain a 320-nm-thick YBCO film, which exhibited Jc=2.44MA/cm2 and Ic=78A/cm. The Ic value has significantly increased from 37A/cm for the evaporated-template.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.