Abstract
The d0 ferromagnetism in wurtzite GaN is investigated by the first-principle calculations. It is found that spontaneous magnetization occurs if sufficient holes are injected in GaN. Both Ga vacancy and Na doping can introduce holes into GaN. However, Ga vacancy has a high formation energy, and is thus unlikely to occur in a significant concentration. In contrast, Na doping has relatively low formation energy. Under N-rich growth condition, Na doping with a sufficient concentration can be achieved, which can induce half-metallic ferromagnetism in GaN. Moreover, the estimated Curie temperature of Na-doped GaN is well above the room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.