Hip simulator testing of the taper-trunnion junction and bearing surfaces of contemporary metal-on-cross-linked-polyethylene hip prostheses.

Abstract

Adverse reaction to metal debris released from the taper-trunnion junction of modular metal-on-polyethylene (MoP) total hip replacements (THRs) is an issue of contemporary concern. Therefore, a hip simulator was used to investigate material loss, if any, at both the articulating and taper-trunnion surfaces of five 32-mm metal-on-cross-linked-polyethylene THRs for 5 million cycles (Mc) with a sixth joint serving as a dynamically loaded soak control. Commercially available cobalt-chromium-molybdenum femoral heads articulating against cross-linked polyethylene (XLPE) acetabular liners were mounted on 12/14 titanium (Ti6Al4V) trunnions. Weight loss (mg) was measured gravimetrically and converted into volume loss (mm3 ) for heads, liners, and trunnions at regular intervals. Additionally, posttest volumetric wear measurements of the femoral tapers were obtained using a coordinate measuring machine (CMM). The surface roughness (Sa) of femoral tapers was measured posttest. After 5 Mc, the mean volumetric wear rate for XLPE liners was 2.74 ± 0.74 mm3 /Mc. The CMM measurements confirmed material loss from the femoral taper with the mean volumetric wear rate of 0.045 ± 0.024 mm3 /Mc. The Sa on the worn area of the femoral taper showed a significant increase (p < 0.001) compared with the unworn area. No other long-term hip simulator tests have investigated wear from the taper-trunnion junction of contemporary MoP THRs. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 108B:156-166, 2020.