The research on the high-speed & low-energy impact under millimetre sized projectile and residual strength under high temperature are rare for SiC/SiC with Environmental Barrier Coatings (EBC). The impact of 2 mm steel projectiles at the speed of 177.5 m/s–252.7 m/s was studied for EBC(Si/Yb2Si2O7/Yb2SiO5)-SiC/SiC with Chemical Vapor Infiltration (CVI) process. The tensile test at 1300 ℃ was conducted on an inert gas protection testing machine. The optical microscope, Scanning Electronic Microscope(SEM), μCT were used to observe the impact and tension after impact(TAI) damage. The results shows that projectile impact has strong effect on EBC peeling, SiC/SiC damage and fracture, and residual-tension strength at 1300 ℃. And the threshold values of impact velocity or energy are different for them. Furthermore, an analysis method for damage evolution by the attachment quantity of oxide was found for EBC-SiC/SiC composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.