Abstract
High-temperature oxidation behaviour of FeCrAl(Y, Pt) alloys was studied in oxygen and oxygen – water vapour (47 vol%) for 18 ks at 1473, 1573 and 1673 K, by mass gain measurements, the amount of spalled oxide, X-ray diffraction, scanning electron microscopy and field emission-transmission electron microscopy – energy dispersive spectroscopy. After oxidation at 1473K for 18 ks in oxygen, the mass gain of the FeCrAl alloy with appropriate addition of both yttrium and platinum was the smallest value, and alumina – alloy interface of the alloy showed good coherency by TEM. After oxidation at 1673K in oxygen – water vapour (47 vol%) for 18 ks, the amount of spalled oxide of FeCrAl0.5Pt alloy was zero. This result is thought to relate to the formation of concentrated platinum layer at the oxide – alloy interface. Spalling of oxide scale on FeCrAl and FeCrAl0.1Y alloys was observed, however, oxide scale on FeCrAl0.5Y alloy showed good adherence during five cycles (one cycle=18 ks) in oxygen – water vapour (47 vol%) at 1573 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.