Abstract
Interfacial reactions between an Al thin film and a single-crystal (001) 6H–SiC substrate were investigated using x-ray diffraction and cross-sectional transmission electron microscopy. Aluminum thin films were prepared by radio-frequency magnetron sputtering method on 6H–SiC substrates at room temperature and then annealed at various temperatures from 500 to 900 °C. A columnar-type polycrystalline Al thin film was formed on a 6H–SiC substrate in the as-deposited sample. No remarkable microstructural change, compared to the as-deposited sample, was observed in the sample annealed at 500 °C for 1 h. However, it was found that the Al layer reacted with the SiC substrate at 700 °C and formed an Al–Si–C ternary compound at the Al/SiC interface. Samples annealed at 900 °C showed a double-layer structure with an Al–Si mixed surface layer and an Al–Si–C compound layer below in contact with the substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.