Abstract
Corrosion behaviour of carbon nanotubes (CNT)-reinforced zirconium yttrium coatings at high temperature under cyclic thermal loading has been investigated in actual coal-fired boiler environment of thermal power plant. The amount of CNT was varied from 0.5 to 6 wt.%, and the coating was developed by the plasma spray technique. The comparative effects of variation in CNT content on hot corrosion behaviour were studied by weight change measurements. The corroded products were then analysed with XRD, FE-SEM with EDAX and X-sectional analysis techniques. The results revealed that the variation in CNT percentile enhances the hot corrosion resistance of boiler steel in actual boiler environment at elevated temperature. The reinforced coatings showed the lower weight gain measurements with the formation of protective scale of oxides during the experiment. Corrosion rate was observed to be reduced with the increased content of CNT in the coating composite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.