Abstract
We report the results of the microstructural characterizations and micro-texture analysis of a lightweight austenitic steel deformed at high strain rate (1200 s−1) using a split Hopkinson pressure bar. Formation of adiabatic shear bands (ASB) and plastic deformation mechanisms within neighboring grains are investigated by high-resolution electron backscatter diffraction (HR-EBSD). HR-EBSD reveals formation of athermal e-martensite and ά-martensite within the shear bands, resulting in the formation of a brittle intersection structure. Crack initiation and propagation is seen in intersection structure. The thermally induced e-martensite follows Shoji-Nishiyama crystallographic orientation relationship with parent austenite phase, while ά-martensite shows Burgers relationship with e-martensite. A detailed examination depicts the presence of deformation twins in grains adjacent to the ASB. Furthermore, strain-induced e and ά martensite are formed in the neighboring grains of ASB. The micro-texture of martensite variants is discussed in ASB and in the neighboring grains.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.