Abstract
AbstractEpoxy resins containing dynamic covalent networks enable recycling of carbon fiber composites. However, the simultaneous realization of high performance and mild condition recycling of composites is still a challenge. In the present work, we mixed citric acid epoxy resin with bisphenol A epoxy resin to form a hybrid resin (DER) that meets the requirements of medium temperature curing epoxy resin, and prepared a carbon fiber reinforced resin composite material (DER@CF) that can rapidly degrade and recycle carbon fibers under mild conditions. The Tg of the DER was 125.67 °C, and the tensile strength (79.63 MPa) was comparable to that of the bisphenol A epoxy resin (79.90 MPa). It degraded rapidly after 2 h in ethylene glycol solution at 120 °C. The tensile strength of DER@CF was 825 MPa, and clean fibers could be obtained after 8 h of treatment in ethylene glycol solution at 120 °C. The results of SEM, Raman and tensile tests showed that the recycled fibers were similar to the original fibers in terms of morphology, chemical structure and mechanical properties. © 2024 Society of Chemical Industry.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.