High-Performance High-$k$$\hbox{Y}_{2}\hbox{O}_{3}$ SONOS-Type Flash Memory

Abstract

In this paper, we propose a novel high-k Y <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> poly-Si-oxide-nitride-oxide-silicon (SONOS)-type flash memory. The structural and morphological features of Y <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films were studied using atomic force microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. These high-k Y <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> SONOS-type memories exhibited large threshold voltage shifting (memory window of 1.9-4.33 V), almost negligible read and gate disturb (threshold voltage shift of ~2-mV operation at V <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">G</sub> = 3 V and V <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">D</sub> = 4 V and ~4-mV operation at V <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">G</sub> =8 V, respectively), excellent data retention (charge loss of ~4% measured time up to 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sup> s and at room temperature, expected ~22% charge loss for ten years at 125degC), and superior endurance characteristics (program/erase cycles up to 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">5</sup> ) because of the higher probability for trapping charge carriers. These Y <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films appear to be a very promising charge trapping layer for high-density two-bit nonvolatile flash memory applications.