Abstract
Transparent and conducting ITO/Ag/ITO (IAI) multilayer coatings were deposited on glass and flexible fluorinated ethylene propylene (FEP) substrates by reactive sputtering using metallic In:Sn (90%:10%) and Ag targets at room temperature. Middle Ag layer thickness was optimized to obtain maximum figure of merit (ϕ) and the optimum Ag layer thickness was found to be ~13nm. The optimized IAI multilayer on glass substrate showed transmittance of ~88.6% and sheet resistance of ~7.1Ω/sq. The transmittance increased to ~91.4% for the IAI multilayer deposited on one side etched glass. The optimized IAI multilayer coating was also deposited on flexible FEP substrates. The electrical, optical, structural and morphological properties of IAI deposited on glass and FEP substrates were compared. IAI deposited on FEP substrate showed transmittance of ~90.2% at λ = 550nm, sheet resistance of ~6.9Ω/sq. and figure of merit of ~52 × 10−3Ω−1. Bending test of IAI deposited FEP proved the high flexibility of IAI multilayer for the flexible transparent electrode applications. Solar selectivity study of IAI on FEP substrate showed it can effectively reflect the higher wavelength region of solar spectrum and can be used as a flexible solar spectrum segregator. Optical haze measurements of IAI coated glass and FEP show that high haze value can be achieved by increasing the roughness on non-coated side of the FEP substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.