Abstract
In this work, we report the copolymerization of a triamine-based benzoxazine and a commercial difunctional epoxy resin, and investigate their synergistic effect on improved thermal properties using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Results showed that a glass transition temperature increase of up to 268 °C was obtained for the copolymer with as low as 25 wt% epoxy. A higher thermal performance was also achieved with an onset degradation of nearly 400 °C and char yield of 39 wt% at 800 °C for the copolymer with 52 wt% epoxy. The behavior was compared to previously reported benzoxazine/epoxy combinations and was found to be advantageous. The curing behavior of different copolymer compositions was also investigated via DSC and a methodology for matching each peak with its corresponding reaction was developed. Results showed that the alternating favorability of the reactions was dependent on the benzoxazine/epoxy ratio. Overall, the prepared PBZ/epoxy copolymers displayed higher thermal stability than their individual components, indicating suitability for a number of potential extended uses including utility in higher temperature applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.