Abstract
High porosity TiAl-based intermetallics were prepared through thermal explosion (TE) from Ti–50Al at.% powders with NaCl as soluble template. The results showed that the space holder particles of NaCl were removed completely in green compacts, and porous Ti–Al materials were synthesized via a low-energy consumption method of TE at a temperature of 600 °C. TiAl was evolved as dominant phase in sintered materials at 1100 °C. With adding 80 vol.% NaCl to Ti–50Al at.% powders, the open porosity was significantly elevated up to 84%. Moreover, the porous materials exhibited a bimodal pore size distribution: large pores (200–500 μm) replicating NaCl particles and small pores (<50 μm) embedded in pore walls. The interconnected small and large pores make open cellular porous TiAl materials, which prescribe them promising for a wide range of applications in separation, heat insulation and catalysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.