Abstract
AbstractMg-doped p-type a-plane GaN films were grown on unintentionally doped a-plane GaN templates by metalorganic vapor phase epitaxy (MOVPE). The Mg concentration in a-plane GaN increased with increasing Mg source gas flow rate. A maximum hole concentration of 2.0 × 1018 cm-3 with a hole mobility of 4.5 cm2/Vs and resistivity of 0.7 Ω·cm were achieved. The activation ratio was 5.0 × 10-2. It was found that a maximum hole concentration in p-type a-plane GaN was higher than that in p-type c-plane GaN. The activation energy of Mg acceptors in p-type a-plane GaN with the maximum hole concentration was found to be 118 meV by temperature-dependent Hall-effect measurement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.