Abstract
Highly ordered microporous films containing polyolefin segment were successfully fabricated via the breath-figure (BF) method using well-defined polymethylene-b-polystyrene (PM-b-PS) diblock copolymers in CS2 under a static humid condition. The effects of molecular weight of diblock copolymers, relative humid, fabrication method and temperature on the morphology of film are investigated. The honeycomb porous films with different pore size (1.2–2.5 μm) were obtained by using PM-b-PS with different PM : PS ratio. The thick (7 μm) and thin (2 μm) films were fabricated via a different process. The film with a pothole-like structure was fabricated when using PM-b-PS with the shortest PS segment. Smaller satellite pores were found to surround the regular micropores of honeycomb films when the BF process was carried out at 28 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.