Abstract
In this study, a synthesis route was developed for preparing highly transparent novel polyimide-nanocrystalline-titania hybrid optical films with a relatively high titania content (up to 50 wt%) and thickness (20–30 μm) from a soluble polyimide 6F-poly(p-hydroxy-imide) (6FPI). It has been demonstrated that the introduction of bulky CF3 groups into polyimide backbones enhanced both solubility and optical transparency. Furthermore, the attachment of hydroxyl groups provided the organic–inorganic bonding and resulted in homogeneous hybrid solutions by controlling the mole ratio of titanium butoxide : hydroxyl groups. AFM, SEM, TEM, and XRD results indicated the formation of well-dispersed nanocrystalline-titania. The flexible hybrid films revealed excellent optical transparency in the visible range, good surface planarity, high thermally dimensional stability, and tunable refractive index. A three-layer anti-reflection coating based on the hybrid films was prepared and revealed a reflectance of less than 0.7% in the visible range, indicating its potential optical applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.