Abstract
We prepared liquid phase exfoliated edge-selectively oxidized graphene (LPEOG) with a high concentration in water (∼14.7 mg ml-1) and a high ratio of a single layer (70%). The edge of graphite was selectively oxidized by step II oxidation of the modified Hummers method, and we subsequently exfoliated the edge-selectively oxidized graphite (EOG) into LPEOG. The edge selective oxidation of the LPEOG was confirmed by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), zeta-potentiometry, Raman spectroscopy, Fourier-transform infrared spectroscopy (FT-IR), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The highly concentrated LPEOG ink can be used in solution processing such as simple drawing or spin casting. Reduced LPEOG showed a higher conductivity (120 000 S m-1) than that of reduced graphene oxide (68 800 S m-1) despite the small lateral size. A transparent conducting film prepared from the LPEOG ink showed a lower surface resistance (∼2.97 kΩ sq-1) at a higher transmittance (>83.0 %T) compared to those of the graphene oxide based film. These results indicate that preservation of π-conjugation of the basal plane of graphene is critical for electrical performance of graphene. Our method facilitates solution processing of graphene for a wide range of applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.