Abstract
Poly(aryl piperidinium) (PAP) anion exchange membranes (AEMs) furnish an important avenue for the commercialization of anion exchange membrane fuel cells (AEMFCs), but their ionic conductivity and alkali resistance still need to be improved. Here, we report the synthesis of PAP AEMs with a branched structure by the acid-catalyzed reaction and compare them with the main-chain AEMs. The experimental results show that the branched AEMs have higher OH− conductivity and alkaline resistance than the poly(terphenyl piperidine) (PTPQ1) AEM. The alkaline stability and OH− conductivity of the AEMs were further improved by a flexible multi-cation crosslinker. The results show that the branched poly(p-terphenyl triphenylmethane 1-methyl piperidine) membrane crosslinked by multi-cation (PTTPQ4-40) shows an excellent OH− conductivity (155.3 mS cm−1) at 80 °C. The OH− conductivity of the PTTPQ4-40 membrane was maintained at 92.1% after soaking in 2 M NaOH for 1080 h at 80 °C. In addition, the peak power density (PPD) of the crosslinked PTTPQ4-40 membrane can reach 656.7 mW cm−2. Compared to the PTPQ1 AEM, the PPD of the crosslinked PTTPQ4-40 AEM is increased by 38.6% in H2-O2. All of the results confirm that the PTTPQ4-40 AEM has excellent fuel cell application prospects.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.