Abstract
In this article, we report the fabrication of Zr-rich high-k ferroelectric hafnium zirconium oxide (HZO) capacitor with TiN as the top and bottom electrodes demonstrating an equivalent oxide thickness (EOT) of 5.7 Å and remanent polarization (Pr) of ~16 μC/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> . High-k-value and low EOT was achieved by utilizing multiphase region of HZO as well as high pressure post metallization annealing (HPPMA). Despite the high-k value of Zr-rich HZO films, the emergence of multiphase region at higher physical-thickness when annealed using rapid thermal annealing (RTA) limits its EOT value. On the contrary, multiphase emerges at a smaller physical thickness in HPPMA due to the formation of more o-phase as revealed by grazing incidence X-ray diffractometer (GIXRD). The smaller physical thickness of HPPMA together with the demonstration of significantly higher dielectric constant (>50) by HZO in the vicinity of multiphase, was therefore, found to be very effective in reducing the EOT.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.