Abstract
AbstractThe higher order structure of stereocomplex‐type poly(lactic acid) melt‐spun fibers of an equimolar blend of poly(L‐lactic acid) and poly(D‐lactic acid) was analyzed with wide‐angle X‐ray diffraction (WAXD) and birefringence measurements. Two different crystalline structures were observed in the fibers: α‐form homocrystals and stereocomplex crystals. The weight fractions of the two crystals were estimated with the WAXD integrated intensity data. The crystalline orientation factors were obtained from the WAXD measurements. Well‐oriented homocrystals formed during a drawing process at the crystallization temperature of the homocrystal. Drawing above this temperature caused the stereocomplex crystal to be formed. The crystalline orientation tended to be lower with increasing drawing temperatures. Through the combination of the intrinsic birefringence and the fractions of the α‐form homocrystals and stereocomplex crystals, the birefringence of the amorphous phase was evaluated. The amorphous birefringence stayed positive and decreased with increasing drawing temperature. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 218–228, 2007
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.