Abstract
The high-temperature wettability and interactions between NbSi-based alloys and Y2O3 ceramics with various microstructures were studied, based on which the corresponding mechanisms were discussed. The results showed that there was a characteristic transition during the high temperature wetting between the alloys and ceramics when the Y2O3 microstructure changed. The rate of spreading of molten NbSi-based alloys on the Y2O3 ceramics was relatively high when the level of open porosity was greater than 20.8%. As the level of open porosity of the Y2O3 ceramics increased from 6.9% to 27.8%, the initial and equilibrium contact angles between the alloys and ceramics increased from 81.3° to 110.0°, and from 60.5° to 93.2°, respectively. TiO and Ti2O phases formed within the alloy matrix of each wetting system. However, as the level of open porosity of the Y2O3 substrates increased, the Ti-oxide content initially gradually decreased and subsequently increased. The alloy in the system with the open porosity level of 20.8% contained the lowest Ti-oxide content while the system with the open porosity level of 6.9% contained the most.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.