High temperature wear resistance of (TiAl)N PVD coating on untreated and gas nitrided AISI H13 steel with different heat treatments

Abstract

The wear resistance of a PVD (Ti 0.7Al 0.3)N coating deposited on an as-received and gas nitrided AISI H13 has been examined by using ball-on-disc tests at room temperature and at 600 °C. In order to determine the influence of a previous heat treatment on this type of steel on the wear resistance of the (Ti 0.7Al 0.3)N coating, two commercial heat treatments were employed which gave rise to the same substrate hardness. Surface microhardness measurements have been carried out to determine the load-carrying capacity of the coated systems. In general, the wear behavior was found to be independent of the nature of the heat treatment applied to the substrate prior to the nitriding process but strongly dependent on the testing temperature. At room temperature, there were small variations between the different systems tested, whereas at high temperatures, clear differences were found between them. At 600 °C, a typical temperature that could be achieved during the aluminum extrusion processes, the nitrided H13 steel/(Ti 0.7Al 0.3)N PVD duplex coating shows a satisfactory wear resistance compared to both the nitrided steel and the steel substrate only coated with (Ti 0.6Al 0.4)N, which exhibited the worst performance. The satisfactory wear resistance observed for the duplex coating system at high temperature is mainly a consequence of two different aspects. Firstly, its higher load-carrying capacity due to the existence of a hard nitrided layer, as well as its high H/E ratio. Both parameters allow the presence of higher elastic strains without the failure of the ceramic layer, which would normally occur in the case of TiAlN PVD coatings deposited directly on the AISI H13 steel. Secondly, the intrinsic characteristics of the coating, i.e. its chemical constitution, which allows the formation of a dense oxide mixture inside the wear track that impedes both its further oxidation and the deterioration of the mechanical properties as consequence of nitrogen diffusion.