Abstract
ABSTRACT Nowadays, studies of high entropy alloys (HEAs) have shown excellent properties. To improve the high-temperature wear resistance of CrMnFeCoNi alloy, refractory carbides (NbC and ZrC, respectively) reinforced CrMnFeCoNi composite coating were prepared by laser cladding (LC), and its wear performance was investigated. The composite coating showed no cracks or other defects that had metallurgical bonding with the substrate. Those coatings exhibited oxidative and adhesive wear mechanisms in reciprocating wear tests at 600°C. In contrast to the strengthening of NbC, the ZrC in the coating rapidly oxidized during high-temperature wear, forming a large amount of ZrO2. These oxides formed in wear promote the formation of a protective film, further improving the oxidation resistance and wear resistance of the coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.