Abstract
Silicon nitride ceramics with ytterbium silicon oxynitride (Yb4Si2O7N2) as secondary phase were fabricated by hot-pressing the powder mixtures, including 50.0 to 97.0 mol% of silicon nitride with a mixture of Yb2O3 and SiO2 (Yb2O3/SiO2 = 4). Sinterability of the materials with Yb2O3 was higher than that with Y2O3 in the same composition of raw powder mixtures. High density materials were obtained under the condition of 50.0 to 89.1 mol% of silicon nitride in raw powder mixtures. Mechanical properties of silicon nitride containing 97.6 mol% of Si3N4 and 2.4 mol% of Yb4Si2O7N2 were measured. Fracture toughness measured by the indentation technique was 5.9 MPam1/2. Bending strength at room temperature and at 1500 °C was 977 MPa and 484 MPa, respectively. The silicon nitride grains consisted of highly elongated rod-like grains and thin needle-like grains. The Yb4Si2O7N2 grains were crystallized at multigrain junctions and bonded close to Si3N4 grains. High strength at high temperature is supposed to be based on the presence of crystalline Yb4Si2O7N2 having a high melting point.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have