High-temperature strain monitoring of stainless steel using fiber optics embedded in ultrasonically consolidated nickel layers∗∗Notice: This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE). The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish

Abstract

Listen

Translate article

Fiber optic sensors have long been considered for use in structural health monitoring of components because of their small size, high accuracy, and their ability to perform spatially distributed strain measurements when embedded within a component or on its surface. The typical method for transferring strain from the component to the fiber is to use an epoxy, which may not survive extended exposure to high temperatures, thus necessitating a more elaborate technique to embed the fibers. This work represents a first step towards using additive manufacturing techniques to embed fiber optic sensors on stainless steel components for high-temperature strain monitoring, including quantification of the differential thermal strains that develop between the fiber and the steel substrate. Copper-coated optical fibers were embedded in nickel layers on top of a stainless steel substrate using an ultrasonic additive manufacturing technique. The embedded fibers showed minimal signal attenuation and clear compressive strain after embedding. Heating the embedded fibers in steps to temperatures of 300 °C–400 °C resulted in measured strains with values between the expected thermal strain in stainless steel and nickel. Finite element simulations confirm the measured strain values and show that the thermal strain depends on the thickness of the nickel layers deposited on top of the stainless steel substrate. While the fibers failed before reaching temperatures of 500 °C, it is suspected that these failures occurred due to a combination of (1) the lack of strain relief, (2) the high-temperature oxidation of the fiber’s copper coating, and (3) improper sizing of the machined channel in which the fiber is placed prior to embedding. If proper coating selection and sizing of the channel can prevent the failures observed in this work, the next step would be to monitor strain during mechanical loading at high temperatures.