Abstract
Systematic variation in the high temperature stability of nanocrystalline anatase powders prepared by chemical vapour synthesis (CVS) using titanium (IV) isopropoxide under varying flow rates of oxygen and helium was obtained by progressively shifting the decomposition product from C 3H 6 to CO 2. The as-synthesised powders were characterised by high temperature X-ray diffraction (HTXRD), simultaneous thermo-gravimetric analyses (STA), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). It was observed that the anatase to rutile transformation temperature progressively increased for samples synthesised at higher O 2/He flow rate ratios. The improved anatase stability was attributed to the presence of incorporated carbon within the titania structure and confirmed by a high temperature carbon desorption peak.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call