Abstract
Slag formation in the bosh and raceway is an important issue in the blast furnace process. SSAB works in Lulea operate with 100 % olivine pellets. A small amount of basic fluxes is added from the top, slag and limestoneare used. To improve the control of slag formation, a concept with injection of BOF slag was evaluated and tested in the LKAB experimental blast furnace (EBF). In this paper, the behaviour of BOF slag as a slag former, when it is top-charged or tuyere-injected, is evaluated based on the results from a laboratory study including reduction tests, softening and melting tests, XRD analyses and SEM analyses. Samples taken from the EBF during excavation, and with a burden probe during operation, are examined. The evaluations show that the melting point of BOF slag is quite low and will not be increased, because of the partial reduction that occurs in the BF shaft. When carbon is present at high temperatures, reduction proceeds and a high basicity slag with a high melting point, consisting of di- and tricalcium silicates, is formed. When pellets with a basicity of B2 ∼ 1 are used, a slag with similar properties can be formed as a result of interaction with the BOF slag. BOF slag in combination with olivine pellets with a low basicity generates a slag with intermediate basicity and the reduction of iron oxides in the slag has a small effect on the melting temperature. The BOF slag decreases the melting point of coal and coke ashes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.