Abstract
Short alumina fiber- and in situ Mg2Si particle reinforced magnesium alloy composites were fabricated by squeeze casting. The in situ Mg2Si particles were formed during the infiltration with the melt into the preforms consisting of the fibers having Si particles attached to their surfaces. The microstructure of the composites and their tensile strength and Young’s modulus in the range from 293 K to 523 K were investigated. The effect of the Mg2Si particles on the tensile properties was examined by comparison with the properties of the fiber-reinforced composite without the Mg2Si particles. Fine Mg2Si particles with a grain size of approximately 5 mm were formed due to the rapid solidification in the permanent mold. The dispersion of the Mg2Si having a high Young’s modulus was found to be effective for improving Young’s modulus of the fiber-reinforced magnesium alloy composite. The experimental value of the composite was in good agreement with the calculated value based on a previously proposed model. The tensile strength of the composite with 18 vol% fibers and Mg2Si particles was higher than that of the conventional fiber-reinforced composite at both room temperature and high temperature. Examination of the fracture surfaces indicated that stress transmission between the fiber and the matrix became easy due to the particles, which reduced the fiber-to-fiber contact. [doi:10.2320/matertrans.MER2008092]
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.