Abstract
BiGaO3 doped BiFeO3–BaTiO3 ceramics were prepared by the traditional solid-phase synthesis process. The phase analysis, microstructure, piezoelectric, ferroelectric, dielectric properties, and thermal stability of 0.7BiFeO3-(0.3 − x)BaTiO3-xBiGaO3 (Abbreviated as BF–BT-xBG) were investigated. The results show that the ceramics have rhombohedral (R) and tetragonal (T) structures. Particle dimensions gradually get bigger with the increase of BiGaO3 concentration, and dense ceramic grains were observed through SEM. Electrical properties of BF–BT-xBG are improved after adding a small amount of BiGaO3: piezoelectric constants d33 = 141 pC/N, electromechanical coupling coefficient kp = 0.314, mechanical Quality Factor Qm = 56.813, dielectric loss tanδ = 0.048, residual polarization intensity Pr = 18.3 µC/cm2, Curie temperature Tc = 485.2 °C, depolarization temperature Td = 465 °C for x = 0.003. The “temperature-piezoelectric performance” curve under in situ d33 indicates that piezoelectric properties d33 increase rapidly with increasing temperature. Remarkably, the piezoelectric response d33 reaches a maximum of 466 pC/N at a temperature T = 340 °C, and afterward, reduces gradually to zero with increasing temperature until 450 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.